Corrosion Behavior of Sprayed Zinc-Aluminum (ZZA) Coatings in Simulated Marine Environment

	Corrosion Behavior of Sprayed Zinc-Aluminum (ZZA) Coatings in Simulated Marine Environment
	Li Yantao 1; Yang Lihui 1; Li Xiao 1,2; Liu Jianguo 3; Hou Baorong 1; Li, YT
	2013-07-01
发表期刊	INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
ISSN	1452-3981
卷号	8 期号:7 页码:9886-9893
文章类型	Article
摘要	The zinc-aluminum coatings were prepared, parts of them were sealed with organic coatings and then the corrosion behavior and mechanism were studied by salt spray test and electrochemical impedance spectroscope (EIS). Scanning Electron Microscope (SEM) was employed to assess the coatings. It showed that the zinc-aluminum coatings were rough and with some defects, which would discount the protection effect. The organic coating would improve the protection through sealing the defects of the metal coating.; The zinc-aluminum coatings were prepared, parts of them were sealed with organic coatings and then the corrosion behavior and mechanism were studied by salt spray test and electrochemical impedance spectroscope (EIS). Scanning Electron Microscope (SEM) was employed to assess the coatings. It showed that the zinc-aluminum coatings were rough and with some defects, which would discount the protection effect. The organic coating would improve the protection through sealing the defects of the metal coating.
关键词	Zinc Organic Coatings Salt Spray Test Thermal Spray Aluminum
学科领域	Electrochemistry
收录类别	SCI
语种	英语
WOS研究方向	Electrochemistry
WOS类目	Electrochemistry
WOS记录号	WOS:000323547600083
WOS标题词	Science & Technology ; Physical Sciences
引用统计	被引频次：4[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.qdio.ac.cn/handle/337002/16358
专题	海洋环境腐蚀与生物污损重点实验室
通讯作者	Li, YT
作者单位	1.Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China 3.China Univ Petr, Coll Pipeline & Civil Engn, Qingdao 266555, Peoples R China
第一作者单位	中国科学院海洋研究所
推荐引用方式 GB/T 7714	Li Yantao,Yang Lihui,Li Xiao,et al. Corrosion Behavior of Sprayed Zinc-Aluminum (ZZA) Coatings in Simulated Marine Environment[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,2013,8(7):9886-9893.
APA	Li Yantao,Yang Lihui,Li Xiao,Liu Jianguo,Hou Baorong,&Li, YT.(2013).Corrosion Behavior of Sprayed Zinc-Aluminum (ZZA) Coatings in Simulated Marine Environment.INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,8(7),9886-9893.
MLA	Li Yantao,et al."Corrosion Behavior of Sprayed Zinc-Aluminum (ZZA) Coatings in Simulated Marine Environment".INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 8.7(2013):9886-9893.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Corrosion Behavior o（448KB）			限制开放	CC BY-NC-SA	浏览