Comparative EIS Study on Atmospheric Corrosion Behavior of Zinc-Aluminum Coated Steels under Cyclic Wet-Dry Conditions | |
Zhao, Xiaodong1,2; Xing, Shaohua3; Yang, Jie1; Zhang, Jie2![]() | |
2014-11-01 | |
发表期刊 | INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
![]() |
卷号 | 9期号:11页码:5877-5884 |
文章类型 | Article |
摘要 | Due to the excellent anticorrosion performance, galvanized steels are widely used in a variety of structural applications for corrosion protection of steel structure exposed to atmospheric environment, especially marine atmosphere. In this work, the corrosion behavior of two representative zinc-aluminum hot-dip coated steels, Galvalume(GL) and Galfan(GF), under cyclic wet-dry conditions, was investigated by weight loss method and electrochemical impedance spectroscopy(EIS) measurement. The wet-dry cycle tests were carried out by exposure to alternate conditions of 1h immersion in seawater and drying for 3h and 11h at 298K and 60% relative humidity (RH). During the wet-dry cycles, the polarization resistance was continuously monitored and its reciprocal was considered as an index of corrosion rate. Results show that the anticorrosion performance of GL coating was better than that of GF coating in all tests. The effects of the formation of stable simonkolleite layer and other influence parameters, such as elemental composition of coating materials, on the corrosion of two coated steels were discussed. |
关键词 | Hot-dip Coated Steel Atmospheric Corrosion Electrochemical Impedance Spectroscopy (Eis) Wet-dry Condition Corrosion Monitoring |
学科领域 | Electrochemistry |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000345261800003 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.qdio.ac.cn/handle/337002/23860 |
专题 | 海洋环境腐蚀与生物污损重点实验室 实验海洋生物学重点实验室 |
通讯作者 | Zhao, XD (reprint author), Zhejiang Ocean Univ, Sch Naval Architecture & Ocean Engn, Zhoushan 316022, Peoples R China. |
作者单位 | 1.Zhejiang Ocean Univ, Sch Naval Architecture & Ocean Engn, Zhoushan 316022, Peoples R China 2.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China 3.Luoyang Ship Mat Res Inst, State Key Lab Marine Corros & Protect, Qingdao 266101, Peoples R China |
第一作者单位 | 中国科学院海洋研究所 |
推荐引用方式 GB/T 7714 | Zhao, Xiaodong,Xing, Shaohua,Yang, Jie,et al. Comparative EIS Study on Atmospheric Corrosion Behavior of Zinc-Aluminum Coated Steels under Cyclic Wet-Dry Conditions[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,2014,9(11):5877-5884. |
APA | Zhao, Xiaodong,Xing, Shaohua,Yang, Jie,Zhang, Jie,&Zhao, XD .(2014).Comparative EIS Study on Atmospheric Corrosion Behavior of Zinc-Aluminum Coated Steels under Cyclic Wet-Dry Conditions.INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,9(11),5877-5884. |
MLA | Zhao, Xiaodong,et al."Comparative EIS Study on Atmospheric Corrosion Behavior of Zinc-Aluminum Coated Steels under Cyclic Wet-Dry Conditions".INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 9.11(2014):5877-5884. |
条目包含的文件 | ||||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Comparative EIS Stud(180KB) | 限制开放 | ODC PDDL | 浏览 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论